Polystyrene-block-polybutadiene copolymers (SB) with 0.5 mass fraction of styrene were studied by electron spin resonance (ESR) of nitroxide spin probes. The influence of the block length ((M) over bar (w) = 12, 000, (M) over bar (w) = 48, 000 and (M) over bar (w) = 83, 000) and the solvation power of casting solvents on the motional dynamics of spin probe were measured over a wide temperature range. Two nitroxide radicals as spin probes were selected: 2,2,6,6-tetramethyl-4-hydroxypiperidine-1-oxyl benzoate (BzONO) and 2,2,6,6-tetramethyl-4-hydroxypiperidine-1-oxyl (Tempol). Irrespective of the spin probe used two ESR spectral components differing in their motional properties above the phase transition of polybutadiene blocks (PB) were observed. The fast component was assigned to spin probes located in polybutadiene-rich domains and the slow component to spin probes in polystyrene-rich domains. The range of two spectral components and the phase transition of the blow ESR component, T-5mT, depend on the block length. The influence of the interphase and accumulation of free volume in the inter phase on the Tempol probe motion was investigated by changing copolymer morphology in the films casted from selective and nonselective solvents. The analysis of the motional heterogeneity from the ratio of the fast and slow motional component presents evidence that in the selective solvent for polystyrene (PS) blocks (2-butanone) the most irregular structure with a large interphase is formed. The difference in fast motion of spin probes indicates that the motional dynamic is related to the change of domain structure. (C) 2003 Elsevier Ltd. All rights reserved.