In situ sum frequency generation vibrational spectroscopy, at varied potentials and polarization combinations, was performed on polycrystalline copper, polycrystalline platinum, and polycrystalline gold samples in 0.5 M HClO4 with 50 mM 5-methylbenzotriazole (5-methylBTAH) added. These studies were performed to determine the orientation of 5-methylBTAH on the surface at different potentials. For copper surfaces, orientation of the molecule on the surface is not affected by potential within the potential window studied (- 500 to -100 mV vs saturated calomel electrode ( SCE)). Sum frequency generation spectra of 5-methylBTAH on platinum show a change in orientation over the potential range studied (- 250 to 750 mV vs SCE). The orientation of the methyl group tilts more toward the plane of the interface as the potential is scanned in the positive direction. This orientation change is correlated to hydrogen coadsorption on the platinum surface at low potentials. 5-Methylbenzotriazole lies in the surface plane or does not orient on gold at lower potentials but the orientation is tilted toward normal at more positive potentials over the potential range studied (-500 to 900 mV vs SCE). To compliment these results, cyclic voltammetry and electrochemical impedance spectroscopy measurements were performed. Cyclic voltammograms of copper show that addition of 5-methylBTAH protects the surface from copper dissolution, increasing the electrochemical window by 450 mV. Cyclic voltammetry of 5-methylBTAH on platinum showed a partial blockage of adsorbed hydrogen and also prevented the adsorption of oxygenated species at 450-600 mV. Cyclic voltammetry on gold shows that 5-methylBTAH blocks oxide formation for 400 mV thus increasing the electrochemical window. Electrochemical impedance spectroscopy has been performed to determine the potential of zero charge of 5-methylBTAH on copper.