The effects of a radiofrequency oxygen plasma pretreatment and residual water content in the substrate on the adhesion of microwave plasma deposited tetramethyldisiloxane thin films on Bisphenol-A polycarbonate (BPA-PC) were investigated. Samples were characterised using a crosshatch adhesion test, optical and electron microscopy, and X-ray photoelectron spectroscopy. It was found that the use of a low power (5 W) and low treatment time (0.1 s) oxygen plasma can improve adhesion while greater treatment times (1-30 s) and higher oxygen plasma powers (40 W) resulted in a decreased level of adhesion. In addition, it was shown that a BPA-PC water content greater than 90 ppm resulted in rapid adhesion failure of deposited films at the substrate-plasma polymer interface during outdoor weathering. All films degraded substantially when exposed to environmental weathering, indicating ageing reactions within the plasma polymer films themselves, and at the bulk polymer-coating interface. (c) 2005 Elsevier B.V. All rights reserved.