A new complex (1) of Prussian blue analogue with the composition of K0.2Mn1.4Cr(CN)(6)center dot 6H(2)O was prepared and characterized structurally as well as magnetically. The crystal structure of complex 1 was determined by X-ray diffraction analysis. The results indicate that complex 1 consists of a 3D cubic lattice similar to those of Mn-3[Cr(CN)(6)](2)center dot xH(2)O, Mn-3[CO(CN)(6)](2)center dot xH(2)O, Cd-3[Cr(CN)(6)](2)center dot xH(2)O, and Cd-3[CO(CN)(6)](2)center dot xH(2)O, Magnetic measurements show that complex 1 is a ferrimagnet with T-c = 66 K. It is interesting to note that the magnetic behavior of complex 1 can be substantially modulated through a dehydration/rehydration treatment. The T-c value of this ferrimagnet increases to 99 K after dehydration reaching a 23.4% weight loss, and it decreases back to 66 K after the dehydrated sample reabsorbs water molecules.