Poly (N-isopropylacrylamide) (PNIPAM) microgel particles labeled with 3-(2-propenyl)-9-(4-N,N-dimethylaminophenyl)phenanthrene (VDP) as an intramolecular fluorescent probe were prepared by emulsion polymerization. The thermo-responsive behavior of the VDP-labeled PNIPAM microgel particles dispersed in water was studied by turbidimetric and fluorescence analyses. The transition temperature of the VDP-labeled PNIPAM microgel particles in water determined by turbidimetric analysis was ca. 32.5 degrees C. The wavelength at the maximum fluorescence intensity of the VDP units linked directly to the microgel particles dramatically blue-shifted around the transition temperature. In addition it gradually blue-shifted even below the transition temperature where there was no change observed in the turbidity. These findings suggest that the gradual shrinking of microgel particles occurs with increasing temperature and the subsequent dramatic shrinking results in the increasing in the turbidity. The transition temperatures of VDP-labeled poly(N-n-propylacrylamide) and poly(N-isopropylmethacrylamide) microgel particles determined by turbidimetric analysis were ca. 23 and ca. 42.5 degrees C, respectively, and their thermo-responsive behavior was similar to that for the VDP-labeled PNIPAM system. In these three systems the microenvironments around the fluorescent probes above the transition temperatures became more hydrophobic than those below the transition temperature, and the estimated values of microenvionmental polarity around the VDP units on their collapsed states were almost the same. (c) 2005 Elsevier Ltd. All rights reserved.