Layered double hydroxides/epoxy (LDHs[EP) nanocomposites were prepared from organo-modified LDHs, a diglycidyl ether of bisphenol A monomer (DGEBA) and amine curing agents. The organo-modified LDHs were obtained by ionic exchange of a magnesium-aluminum carbonate LDH in an acid medium. X-ray diffraction and transmission electron microscopy showed a dispersion of the layers at a nanometer scale, indicating the formation of LDH/EP nanocomposites. The thermal degradation and flame resistance properties of LDH/EP nanocomposites, montmorillonite-epoxy (MMT/EP) nanocomposites, LDH/EP microcomposites and aluminum hydroxide-epoxy microcomposites were compared by thermogravimetrical analyses, simultaneous thermal analyses, UL94 and cone calorimeter tests. Only LDH/EP nanocomposites showed self-extinguishing behavior in the horizontal UL94 test; LDH/EP microcomposites and MMT/EP nanocomposites samples burned completely showing that the unique flame resistance of LDH/EP nanocomposites is related to both the level of dispersion and the intrinsic properties of LDH clay. Furthermore, cone calorimeter revealed intumescent behavior for LDH/EP nanocomposites and a higher reduction in the peak heat release rate compared to MMT/EP nanocomposites. (c) 2005 Elsevier Ltd. All rights reserved.