A paraffin/expanded graphite composite phase change thermal energy storage material was prepared by absorbing the paraffin into an expanded graphite that has an excellent absorbability. In such a composite, the paraffin serves as a latent heat storage material and the expanded graphite acts as the supporting material, which prevents leakage of the melted paraffin from its porous structure due to the capillary and surface tension forces. The inherent structure of the expanded graphite did not change in the composite material. The solid-liquid phase change temperature of the composite PCM was the same as that of the paraffin, and the latent heat of the paraffin/expanded graphite composite material was equivalent to the calculated value based on the mass ratio of the paraffin in the composite. The heat transfer rate of the paraffin/expanded graphite composite was obviously higher than that of the paraffin due to the combination with the expanded graphite that had a high thermal conductivity. The prepared paraffin/expanded graphite composite phase change material had a large thermal storage capacity and improved thermal conductivity and did not experience liquid leakage during its solid-liquid phase change. (c) 2005 Elsevier Ltd. All rights reserved.