Journal of Vacuum Science & Technology A, Vol.23, No.4, 790-795, 2005
Structure and magnetism of ultrathin Co film grown on Pt(100)
Ultrathin Co films were deposited on Pt(100) at room temperature in ultrahigh vacuum, and investigated in situ by low-energy electron diffraction, scanning tunneling microscopy (STM), and surface magneto-optic Kerr effect. The Co film was grown into a wedge shape to provide a continuous change of the film thickness. We find that the Co film forms single-crystal ultrathin films at least up to 5 monolayers (ML). For as-grown films, we observe only in-plane magnetization. After annealing the film, the Co film develops a perpendicular magnetic anisotropy, leading to a spin reorientation transition at 2.7 ML Co thickness. STM measurements were performed at room temperature both before and after annealing the film. We found very different surface morphology and alloy formation after the film annealing, and attribute the perpendicular magnetic anisotropy to the formation of the Co-Pt alloy layer at the Co/Pt(100) interface. (c) 2005 American Vacuum Society.