Electropolymerization of o-(CH3O)(2)C6H4 (Veratrole) in dry acetonitrile/tetrabutylammonium tetrafluoroborate at platinum electrode, yields a green polymeric conducting solid. As the pressure is increased, the material becomes more conductive, but sharp changes towards lower conductivity occur at 4.2 and 6.2 metric tons pressure, probably due to phase transitions. The photoconductivity shows an exponential increase as temperature is increased, but it shows reversible changes at 200 K, 225 K and 250 K during slow warming, also attributable to phase transitions. Photoconductivity of Polyveratrole increases with the radiation frequency, being higher under blue light than under red of infrared radiation and there is a linear increase of photoconductivity with radiation density. Conductivity transients show that the conductivity increases exponentially with time to the saturation point within few minutes, and it also decreases exponentially when the light is turned off and the circuit is open. This behaviour can be explained by formation and encounter of electron and hole as current carriers. A preliminary study indicates a piezoelectric effect for the material. absorption spectroscopy allowed the measurements of the material band gap.