Light has been used to induce photochemical changes in the surface chemistry of porous polymer microstructures giving rise to a substantial change in volume. When illumination is asymmetric, this results in light-directed motion of the structure. Swellable trimethylolpropane trimethacrylate crosslinked poly(2-hydroxylethyl methacrylate) microstructures were constructed by azo-bis-isobutyronitrile photopolymerization using a 20 x 0.5 NA microscope objective and 365 nm laser excitation. Structures were aminiated with glycine and protected with the photolabile group 4-nitroveratryloxycarbanyl (N-VOC). Addition of NVOC resulted in a volume increase > 10 % when performed in the solvent N,N'-dimethylformamide. Photochemical cleavage of NVOC using asymmetric illumination of a cone-shaped microstructure with a 365 nm laser induced polymer shrinkage in excess of 4 % at the base of the cone and resulted in a maximum velocity of 1 mm/s at the tip of the cone. Symmetric illumination gave rise to displacement of solvent from the microstructure due to shrinkage with a velocity in excess of 0.01 mm/s. This system could in principle be used for light-directed movement of micromechanical systems, optical control of microfluidics, or light activated chemical delivery.