The water-soluble defoamers were fabricated by the mixing polyol, modified silicon resin, silicon resin and surfactant. For the defoamers, the various properties such as phase-separation time, viscosity and defoamerability were examined. The phase-saparation time of PPG mixtures was found to be PPG 400>PPG 3,000>PPG 1000. When PPG 1000 was mixed, mixtures represented the excellent defoamerability The phase-saparation time of silicon resin mixtures was TSF-451-350> TSF-451-200> TSF-451-50. As more of high molecular silicon resin was mixed, the resulting mixtues showed reduced defoamerability. When the TSF-451-50 was mixed, the mixture's volume was increased because of the reduction of solubility. The modified silicon resin was smoothly dispersed in water, but the compatibility with PPG was not good. The defoamerability of surfactant was SPAN 20> SPAN 60> SPAN 80. SPAN 80 showed good miscibility for the silicon resin, but not good for YAS 6406 or PPG 1000.