The orientation behavior of isotactic polypropylene (iPP) in alpha- and beta-crystal form was investigated by rheo-optical Fourier transformed infrared (FTIR) spectroscopy. This method enabled quantification of the degree of orientation as a feature of structural changes during uniaxial elongation in not only the crystalline phase but also the amorphous one. Molecular orientation mechanisms can be successfully derived from experimental results. Generally, three mechanisms were detected for iPP: (1) interlamellar separation in the amorphous phase, (2) interlamellar slip and lamellar twisting at small elongations, and (3) intralamellar slip at high elongations. The third mechanism was favored by alpha-PP, whereas beta-PP favored the second mechanism, which, in fact, was responsible for the different mechanical properties of both materials at the macroscopic level. On the other hand, crystallization conditions may have significantly affected the amorphous orientation. Nevertheless, for both iPP types the chains in the amorphous phase always oriented less than did those in the crystalline phase. (C) 2004 Wiley Periodicals, Inc.