New aromatic diamine with cyclohexane cardo group substituted with trifluoromethyl group in the side chain, 1,1-bis[4-(4-amino-2-trifluoromethylphenoxy)phenyl]cyclohexane (II), was prepared through the nucleophilic substitution reaction of 1,1-bis(4-hydroxyphenyl)cyclohexane and 2-chloro-5-nitrobenzotrifluoride in the presence of potassium carbonate, to yield the intermediate dinitro compound I, followed by catalytic reduction with hydrazine and Pd/C to afford the diamine II. Fluorinated polyimides (IVa-g) were prepared from the II with various aromatic dianhydrides via thermal or chemical imidization of poly(amic acid). These polyimides had inherent viscosity ranging from 0.72 to 1.16 dl/g and showed excellent solubility in a variety of organic solvents. They were soluble in a concentration of 10% in the amide polar solvent, and 1-5% in the other testing solvents. IV films showed good mechanical properties, excellent thermal stability. The 10% weight loss temperature was above 476 degreesC in nitrogen or air, and the glass transition temperature was recorded at 214-278 degreesC. In comparison of the IV series with the analogous nonfluorinated polyimides (V series) based on 1,1-bis[4-(4-aminophenoxy)phenyl]cyclohexane (II), IV series revealed better solubility, lighter-colored and lower dielectric constants and moisture absorptions. Their films had cutoff wavelengths in the range of 364-414 nm, b* value (a yellowness index) ranging from 3.3 to 66.3, dielectric constants of 3.02-3.55 (1 MHz), with moisture absorption of 0.16-0.36 wt%. (C) 2004 Elsevier Ltd. All rights reserved.