The structure and mechanical properties of highly oriented films of a miscible blend of syndiotactic polystyrene and poly(2,6-dimethylphenylene-1,4-oxide) (sPS/PPO) were studied in the composition range of sPS/ PPO = 10/0 to 5/5. The oriented films were prepared by stretching the amorphous films of the blends. Wide-angle X-ray diffraction and polarized FTIR spectroscopy were used to analyze the amount of mesophase and molecular orientation. Drawing of the amorphous films of sPS and sPS/PPO blend induced a highly oriented mesophase. The mesophase content increases with increasing draw ratio and becomes nearly constant above a draw ratio of 3. Under the same draw ratio, the mesophase content decreases with increasing PPO content. The orientation function in the mesophase is as high as 0.95-0.99 irrespective of the composition and draw ratio. On the other hand, the orientation of molecular chains in the amorphous phase and mesophase increases with increasing draw ratio, and it decreases with increasing PPO content. The drawn films of pure sPS show high strength and high modulus in the drawing direction, but exhibit low strength in the direction perpendicular to the drawing. In the case of sPS/PPO = 7/3 blend, however, the ultimate strength in the perpendicular direction was dramatically improved compared with that of pure sPS and the ultimate strength in the parallel direction was similar to that for the oriented pure sPS. The improved mechanical properties in the sPS/PPO blends were discussed in relation to the structural characteristics of the sPS/PPO blend system. (C) 2004 Wiley Periodicals, Inc.