Latexes of carboxylated styrene-butadiene rubber were prepared via batch emulsion copolymerization with different amounts of acrylic acid in the absence of emulsifier. The effect of acid monomer was investigated in the particle formation and growth. It was observed that the amount of acrylic acid strongly affected the particle formation. The number of particles and thus polymerization rate increased with increasing of the acid content. There was no significant difference in the polymerization rate per particle in all experiments. The results show that in this case particle growth process is less dependent on the acrylic acid amount in comparison with its influence on nucleation stage and then particle number. Several parameters such as polymerization rate and number of latex particle per unit volume of the aqueous phase were calculated. Attempt was made to evaluate the average number of growing chain per particle. Also average particle diameter of the above carboxylated SBR latexes was obtained through some calculations from the direct measurement of average particle diameter in the swollen state by light scattering technique for the first time. (C) 2004 Elsevier Ltd. All rights reserved.