The influence of lignin (L) on the thermal properties and kinetics of crystallization of isotactic polypropylene (PP) is reported in this article. PP blends containing 5 and 15 wt % of L were prepared by mixing the components in a screw mixer. An increase of the thermal degradation temperature of the blends was observed as a function of L content. The crystallization and thermal behavior of the pure PP and of the PP/L blends were analyzed by differential scanning calorimetry (DSC). Isothermal crystallization kinetics were described by means of the Avrami equation, which suggests a three-dimensional growth of crystalline units, developed by heterogeneous nucleation. The isothermal growth rate of PP spherulites was studied using a polarizing optical microscope. The enhancement of PP crystallization rate for the PP/L blends was observed and ascribed to the nucleating action of lignin particles. Non-isothermal crystallization kinetics were applied, according to the results elaborated by Ziabicki and the method modified by Jeziorny. The kinetic crystallizability of the PP is not influenced by the L present in the blend. In the presence of L, PP can simultaneously crystallize in both the a and P crystalline forms, and the ratio between the a and 0 forms was determined by X-ray diffraction analysis. Two melting peaks relative to the two crystalline form of PP were observed for the PP/L blends, for all isothermal crystallization temperatures investigated by means of DSC. The equilibrium melting temperature for a-form of pure PP was obtained. (C) 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 1435-1442,2004.