The epoxy resins were toughened by 4-24 phr polyester with average molecular weight 1.9X10(4) g/mol in this investigation. The mechanical properties were examined and dynamic mechanics analyses were performed for the epoxy resins before and after the modification. The toughening mechanism of polyester to epoxy resin is discussed in light of the scanning electronic microscopy observation of the fracture surfaces. The results showed that the impact strength and tensile strength of the modified epoxy resin were remarkably greater than those of the unmodified cured epoxy resin. The most suitable composition for the modified epoxy resin was the addition of 16 phr polyester, which led to 138 and 46% increments in the impact strength and the tensile strength, respectively. And the mechanical properties depended greatly on the congregating state of polyester added. The polyester dispersing in the epoxy matrix was amorphous when its addition was less than or equal to 12 phr, and was sphere crystals when the addition was over 16 phr. (C) 2003 Wiley Periodicals, Inc.