Flexible, transparent, and crosslinked polymer films were synthesized by polymerization of PEG-modified urethane acrylate using a simple method. A series of novel solid polymer electrolytes and gel electrolytes were prepared based on this type of polymer film. To understand the interactions among salt, solvent, and polymer, the swelling behaviors of the crosslinked polymer in pure propylene carbonate (PC) and liquid electrolyte solutions (LiClO4/PC) were investigated. The results showed that the swelling rate in the electrolyte solution containing moderate LiClO4 was greater than that in pure PC. Thermogravimetric analysis (TGA) also supported the interaction between the solvent and polymer. The morphology and crystallinity of the crosslinked polymer and polymer electrolytes were studied using atomic force microscopy (AFM) and wide-angle X-ray diffraction (WAXD) spectroscopy. The effects of the content of the electrolyte solution on the ionic conductivity of gel electrolytes were explored. The dependence of the conductivity on the amount of the electrolyte solution was nonlinear. With a different content of the plasticizer, the ionic conduction pathway of the polymer electrolytes would be changed. The best ionic conductivity of the gel electrolytes, which should have good mechanical properties, was 4 x 10(r-3) S cm(-1) at 25degreesC. (C) 2003 Wiley Periodicals, Inc.