Nano-structured poly(e-caprolactone) (PCL) nonwoven mats were prepared by electrospinning process. In this study, three types of solution were used. One dissolved in only methylene chloride (MC), the second dissolved in mixture of MC and N,N-dimethylformamide (DMF), the third dissolved in mixture of MC and toluene. MC, toluene and DMF are a good, poor, and nonsolvent for PCL, respectively. For the MC only, electrospun fibers had very regular diameter of about 5500 nm, but electrospinng is not facilitated. For the mixture of MC and DMF, electrospinning is certainly enhanced as well as fiber diameter decreased dramatically as increasing DMF volume fraction. It was due to high electric properties of solution such as dielectric constant and conductivity. Whereas, as increasing toluene volume fraction, electrospinning is strictly restricted due to very high viscosity and low conductivity. As the results, it has regarded that solution properties is one of the important parameter in electrospinning. Properties such as conductivity, surface tension, viscosity and dielectric constant of the PCL solutions prepared from three types of solvent system were studied. The morphology, crystallinity and mechanical properties of electrospun PCL nonwoven mats were characterized by scanning electron microscopy (SEM), wide angle X-ray diffraction (WAXD) and universal testing method (UTM), respectively.