A new class of silica/polyimide nanocomposites was successfully prepared by the sol-gel reaction, tetraethoxysilane, (TEOS), was hydrolyzed by the water released from imidization at low and high temperature. Silica particles with diameter of around 30-50 nm were observed in the hybrid films by scanning electron microscopy. The flame retardance, decomposition temperature and glass transition temperature of the film increased with increasing silica content. The tensile strength increased slightly while the elongation at break of the films decreased with increasing silica content.