Three samples of silica of different pore structure-predominantly microporous, S1; mesoporous, S2; and nonporous, S3-were modified with zirconium phosphate and examined. Pore structure analysis showed that modification had taken place in wider pores of S1 leaving a totally microporous sample, and in large pores of S2 giving a mesoporous sample of narrower pore size distribution. The modification of the nonporous sample decreased the surface area and pore volume to a lower extent than in the other two samples, but resulted in a surface of lower energy toward N-2. The different distribution of surface silanol groups on the surfaces of different porosity may result in variable pictures on the modified surfaces as reflected in the differences observed in Bronsted acidity of modified surfaces. The use of these modified silica samples for amino acid adsorption (L-glutamic acid and L-alanine) indicated that both the isoelectric point of the amino acid and the distribution of surface groups on modified solids are controlling the adsorption process.