The solution behaviour of a new mesogenic side group polyacrylate in tetrahydrofuran and toluene has been investigated by static and dynamic light scattering. In the dilute regime the polymer behaves as typical polydisperse linear chains in good solvent and the dynamics is dominated by a single fast mode. Cluster formation was detected starting at a concentration around 50 g l(-1). It seems to be independent of the solvent as well as of polymer molecular weight. In the semidilute regime, the behaviour of the reduced osmotic modulus leads to the conclusion that repulsion between the chains is stronger than in linear macromolecules. The appearance of larger clusters was revealed above a characteristic concentration and is slightly dependent on the polyacrylate molecular weight. The dynamics was generally characterised by a fast mode related to the cooperative diffusion and by a slow mode associated with large clusters, The existence of a network of multiconnected clusters is envisaged with increasing solution concentration.