The crystalline quality and ferroelectricity of the Pb(Zr,Ti)O-3 (PZT) films deposited on the metallic LaNiO3 (LNO) and Pt electrodes were comparatively analyzed to investigate the possibility for their application to non-volatile memory devices. LNO thin films were successfully deposited on various substrates by using r.f. magnetron sputtering even at a low temperature ranging from 250 to 500 degreesC, and the ferroelectric PZT thin films were spin-coated onto the LNO and Pt bottom electrodes. Metallic LNO thin films exhibited [100] orientation irrespective of the substrate species and PZT films coated onto LNO films had highly a-and c-axis orientations, while those with Pt bottom electrode were polycrystalline. PZT films with LNO bottom electrode had smaller grain size and larger dielectric constant compared to those grown on the Pt electrode. The ferroelectric thin films fabricated on LNO bottom electrode displayed an asymmetric D-E hysteresis loop, which was explained by the defect effects formed at the interface. Especially, the LNO/PZT/LNO capacitor was found to significantly improve the polarization fatigue and the effects of the LNO electrodes to the fatigue were discussed.