The effect of gamma-radiation on a perfluoroalkoxy (PFA) resin was examined using solid-state high-speed magic angle spinning (MAS) F-19 NMR spectroscopy. Samples were prepared for analysis by subjecting them to gamma-radiation in the dose range 0.5-3 MGy at either 303, 473, or 573 K. New structures identified include new saturated chain ends, short and long branches, and unsaturated groups. The formation of branched structures was found to increase with increasing irradiation temperature; however, at all temperatures the radiation chemical yield (G value) of new chain ends was greater than the G value of long branch points, suggesting that chain scission is the net process.