A new series of network liquid crystal polymers were synthesized by graft copolymerization of the difunctional mesogenic monomer 4-allyloxy-benzoyloxy-4'-allyloxybiphenyl (M) upon polymethylhydrosiloxane (PMHS). Monomer M acted not only as a mesogenic unit but also as a crosslinker for the network polymers. The chemical structures of the polymers were confirmed by IR spectroscopy. DSC, TGA, and X-ray scattering were used to measure their thermal properties and mesogenic properties. The glass transition temperature (T-g) of these network liquid crystal polymers was increased when the monomer was increased, and T-d (temperature of 5% weight loss) at first went up and reached a maximum at P, then went down. The slightly crosslinked polymers (P, P,) show rubber-like elasticity, so it was called liquid-crystal elastomer. Network polymers will lose elasticity property with a highly crosslinked degree, and turn into thermosetting polymers (P-4, P-5). All polymers exhibited a smectic texture by X-ray scattering.