Single crystal of butyl branched polyethylene with various molecular weight formed from the melt in the presence of electric field was studied. It was found that electric field influenced morphology and structure of the butyl branched polyethylene single crystals formed. The lateral habits of the single crystals were circular shape, which was different from truncated lozenge or lenticular shape single crystals formed from the melt in the absence of electric field. The stems in the single crystals formed in the presence Of electric field were perpendicular to the basal plane of the single crystals, which was different from chain tilting in single crystals formed from the melt in the absence of electric field. The electron diffraction patterns showed that the structure of the circular single crystals was a quasi-hexagonal with looser chain packing. This looser chain packing was favorable to thickening growth of single crystals through chain sliding diffusion. The thickness of the single crystals was much larger and depended on molecular weight. It indicated that the single crystal in the presence of electric field should be an extended chain type Single crystal.