2,2'-Azobis[N-(2-propenyl)-2-methylpropionamide] (APMPA) with two carbon-carbon double bonds and an azo group was copolymerized with vinyl benzoate (VBz) at 60 degreesC, resulting in azo groups containing VBz/APMPA prepolymers and crosslinked polymers as soluble and insoluble polymeric azo initiators, respectively. The polymerization characteristics of APMPA as a novel diallyl monomer were clarified with the rate and degree of polymerization and the monomer reactivity ratios. The gelation behaviors in VBz/APMPA crosslinking copolymerizations were examined in detail with a comparison of the actual gel point and the theoretical gel point calculated according to Stockmayer's equation with the tentative assumption of equal reactivity for both vinyl groups belonging to VBz and APMPA. The effectiveness of the resulting branched or crosslinked poly(VBz-co-APMPA)s as soluble or insoluble polymeric azo initiators, respectively, at providing graft polymers through the cleavage of azo groups at an elevated temperature was examined by the polymerization of allyl benzoate at 120 degreesC.