Novel poly(ethylene terephthalate) (PET) copolyesters, abbreviated PEDMBT, containing optically active (2S,3S)-2,3-dimethoxy-1,4-butanediol (DMBD) as the second comonomer were investigated. Copolymers with ethylene glycol to DMBD ratios between 95/5 and 50/50 as well as the two parent homopolymers, PET and PDMBT, were prepared by a two-step melt polycondensation. The resulting copolymers were found to approximately have the composition of the polymerization reaction feed and a random microstructure. Polymer intrinsic viscosities varied from 0.4 to 0.6 dL g(-1) with weight-average molecular weights ranging from 16,000 to 44,000. PEDMBT copolyesters were distinguished in being much more soluble than PET and showing an increasing affinity for water with the content in dimethoxy groups. According to the asymmetric constitution of DMBD, they displayed optical activity in solution. Both melting and glass-transition temperatures of the copolyesters were observed to steadily decrease with the content in DMBD. PEDMBTs were found to be crystalline for contents in DMBD up to 30 mol %. Both powder and fiber X-ray diffraction revealed that the same crystalline structure is shared by PET and the crystalline copolyesters. The homopolyester PDMBT resulted in becoming a polymer with a crystallinity comparable to PET but with a significantly different crystalline structure.