In this paper the influence of notch acuity and test temperature on the impact behavior of aluminum alloy 6061 is presented and discussed. Notch angles of 45 degrees, 60 degrees, 75 degrees and 90 degrees were chosen for a standard charpy impact test specimen containing two such notches positioned at right angles to the applied load. For a given angle of the notch the dynamic fracture toughness increased with an increase in test temperature. At a given test temperature, the impact toughness of a ductile microstructure decreased with an increase in notch severity. For the least severe notch dynamic fracture surfaces revealed the occurrence of localized mixed-mode deformation at the elevated temperature. An increase in notch severity resulted in essentially Mode-I dominated fracture at all test temperatures. The results are discussed in light of alloy microstructure, fracture mechanisms and deformation field ahead of the advancing crack tip.