Enargite (Cu3AsS4) was leached faster by bacteria in sulfuric acid medium (pH 1.6) with added ferric sulfate than by chemical leaching at the same or higher iron concentration. During chemical leaching with ferric iron, the copper dissolution rate decreased from an initial value of 0.03% per hour to a value of 0.002% per hour. Enargite is oxidized to elemental sulfur and dissolved arsenic (As3+ and As5+). Less than 10% of sulfur is oxidized to sulfate. The arsenic and copper dissolutions observed in bacterial leaching experiments suggest the existence of a specific bacterial action on the leaching of enargite, demonstrated by the ability of bacteria to oxidize enargite at very low concentration of dissolved iron and by the higher dissolution rate obtained in bacterial leaching compared to chemical ferric leaching.