Three supported La0.8Sr0.2MnO3+x catalysts were prepared, one supported on lanthanum-stabilised alumina and two supported on a NiAl2O4 spinel. The catalysts were characterised using X-ray diffraction, transmission electron microscopy and surface area measurements following heat-treatments at temperatures up to 1200 degreesC in air. In the alumina-supported catalyst, a reaction occurred between the active phase and the support at high temperatures, indicating that these materials would be unsuitable for high temperature catalytic combustion. Only in the NiAl2O4-supported catalysts were the supported perovskite phases found to be stable at high temperature. These catalysts showed good methane combustion activity.