Changes occurring in jute fibers when treated with a 5% concentration of a NaOH solution for 0, 2, 4, 6, and 8 h were characterized by weight loss, linear density, tenacity, modulus, FTIR, and X-ray measurements. A 9.63% weight loss was measured during 2 h of treatment with a drop of hemicellulose content from 22 to 12.90%. The linear density value showed no change until 2 h of treatment followed by a decrease from 33.0 to 14.5 denier by 56% after 6 h of treatment. The tenacity and modulus of the fibers improved by 45 and 79%, respectively, and the percent breaking strain was reduced by 23% after 8 h of treatment. X-ray diffractograms showed increase in crystallinity of the fibers only after 6 h of treatment, while FTIR measurements showed much of the changes occurring by 2 h of treatment with an increased amount of OH groups. By measuring the rate of change of the modulus, tenacity, and percent breaking strain with the time of treatment, a clear transition was apparent at 4 h of treatment with the dissolution of hemicellulose, causing a weight loss and drop in the linear density before and development of crystallinity with an improvement in the properties after the transition time.