The miscibility and crystallization behavior of poly(ether ether ketone ketone) (PEEKK)/poly(ether imide) (PEI) blends prepared by melt-mixing were investigated by differential scanning calorimetry. The blends showed a single glass transition temperature, which increased with increasing PEI content, indicating that PEEKK and PEI are completely miscible in the amorphous phase over the studied composition range (weight ratio: 90/10-60/40). The cold crystallization of PEEKK blended with PEI was retarded by the presence of PEI, as is apparent from the increase of the cold crystallization temperature and decrease of the normalized crystallinity for the samples anealed at 300 degreesC with increasing PEI content. Although the depression of the apparent melting temperature of PEEKK blended with PEI was observed, there was no evidence of depression in the equilibrium melting temperature. The analysis of the isothermal crystallization at 313-321 degreesC from the melt of PEEKK/PEI (100/0, 90/10, and 80/20) blends suggested that the retardation of crystallization of PEEKK is caused by the increase of the crystal surface free energy in addition to the decrease of the mobility by blending PEI with a high glass transition temperature.