Temperature modulated dynamic mechanical analysis (TMDMA) was performed in the same way as temperature modulated DSC (TMDSC) measurements. Temperature modulation with amplitude 0.5 K and period 20 min was realised by a series of linear heating and cooling cycles (saw-tooth modulation). As in TMDSC TMDMA allows for the investigation of reversible and non-reversible phenomena in the melting: and crystallisation region of polymers. The advantage of TMDMA compared to TMDSC is the high sensitivity for small and slow changes in crystallinity, e.g. during re-crystallisation. The combination of TMDMA and TMDSC yields new information about local processes at the surface of polymer crystallites. It is shown that during and after isothermal crystallisation the surface of the individual crystallites is in equilibrium with the surrounding melt.