Simultaneous emanation thermal analysis (ETA), DTA and TG measurements show that upon mechanical grinding the structure of gibbsite changes from well-crystallized to amorphous, with a small proportion undergoing mechanochemical dehydration to form amorphous alumina, a precursor of eta-Al2O3, which then transforms to alpha-alumina by, it is proposed, a diffusion mechanism.