HWAHAK KONGHAK, Vol.12, No.1, 33-36, February, 1974
NiO-Al2O3계 고체반응기구에 대하여
Solid Phase Reaction Mechanism in NiO-Al2O3 System
The reaction rate constant in the spinel formation reaction from nickel oxide and alumina polycrystalline was measured at temperatures ranging from 1,050 to 1,300℃ in air.
Comparision of experimental and theoretical values of the rate constants showed that the diffusion process of aluminium ions through the spinel layer was rate controlling.