Dielectric and viscoelastic relaxation measurements have been performed on poly(2-chloroethyl methacrylate) and poly(3-chloropropyl methacrylate) between -140-degrees-C and the glass transition temperatures. The splitting of the dipolar relaxations from those of conductive origin in the dielectric spectra was performed.