The intercalates of the M(x)V(x)(IV)V(1-x)(V)OPO(4).yH(2)O (M=Li, Na, H) type were prepared. The structure of products was studied by X-ray diffraction and DTA. The consecutive rise of the stages was observed during intercalation. The decrease of conductivity with increasing content of the guest was observed by the impedance measurements.