Nonmetal mesoporous carbon exhibits environment friendliness and low cost, which attract much attention in energy storage and conversion. In this work, a N, P-doped mesoporous carbon (NPMC-T) was synthesized by the SiO(2)hard template. The mesoporous structure and high N, P content for NPMC-T are beneficial to expose more active sites and accelerate electron transfer, and contribute to exhibit remarkable electrocatalytic activity for supercapacitors and hydrogen evolution reaction application. NPMC-800 is applied as electrode material for supercapacitors and exhibits high specific capacitance (219 F g(-1)at 1 A g(-1)). Meanwhile, the NPMC-T is used as electrocatalyst for HER and shows the good electrocatalytic performance with small Tafel slope of 52 mV dec(-1), low overpotential of 298 mV (10 mA cm(-2)) than that of most other reported analogous catalysts, and excellent stability (after 2000 cycles). This effective capability of N, P-doped multifunctional mesoporous carbon materials is expected to promote the application in supercapacitors and hydrogen evolution reaction widely.