The content of strain-induced martensite in austempered ductile iron has been quantitatively determined using three different kinds of neutron methods: (1) high-resolution powder diffraction with subsequent standard Rietveld refinement, (2) phase quantification using pole figure measurements and (3) Bragg edge neutron transmission. The accuracy and scope of applications of these neutron diffraction and imaging techniques for phase quantification have been compared and discussed in detail. Combination of these methods has been confirmed as effective for dealing with problems like peak overlap in multi-phase materials and texture formation after plastic deformation. Further, the results highlight the potential of using single peak pole figure data for quantitative phase analysis with high accuracy.