In this work, K-Fe bimetallic catalyst supported on porous biomass char was synthesized via a one-step synthesis method by pyrolysis of biomass (peanut shells) after impregnation of a small amount of potassium ferrate (PSC-K2FeO4), and was evaluated for the cracking of biomass pyrolysis tar. Control experiments using the pure char (PSC) and char-supported catalysts after impregnation of KOH (PSC-KOH) and FeCl3 (PSC-FeCl3) were also performed for comparison. The as-prepared PSC-K2FeO4 possessed a porous structure with the dispersion of particles/clusters of Fe metal, K2CO3 and KFeO2 on the char support. Tar cracking experiments showed that the PSC-K2FeO4 exhibited excellent catalytic activity on the cracking of biomass pyrolysis tar in the temperature range of 600-800 degrees C, and the obtained tar conversion efficiencies were obviously higher than that in the control experiments, particularly at relatively lower temperatures (600 and 700 degrees C). The yields of combustible gas compounds including CO, H-2 and CH4 increased significantly using PSCK2FeO4 as the catalyst due to the enhanced tar cracking and reforming reactions. The porous structure and the active crystal structures of the spent catalyst were well retained, indicating the potential for efficient and long-term utilization of the catalyst in tar cracking. PSC-K2FeO4 exhibited excellent reusability during the five times reuse under the same conditions without regeneration, which showed almost no obvious decrease in the tar conversion efficiency and gas yields. (C) 2020 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.