The effects of introducing a passivation layer at the rear of ultrathin Copper Indium Gallium di-Selenide Cu(In,Ga)Se-2 (CIGS) solar cells is studied. Point contact structures have been created on 25 nm Al2O3 layer using e-beam lithography. Reference solar cells with ultrathin CIGS layers provide devices with average values of light to power conversion efficiency of 8.1% while for passivated cells values reached 9.5%. Electronic properties of passivated cells have been studied before, but the influence of growing the CIGS on Al2O3 with point contacts was still unknown from a structural and morphological point of view. Scanning Electron Microscopy, X-ray Diffraction and Raman spectroscopy measurements were performed. These measurements revealed no significant morphological or structural differences in the CIGS layer for the passivated samples compared with reference samples. These results are in agreement with the similar values of carrier density (similar to 8 x 10(16) cm(-3)) and depletion region (similar to 160 nm) extracted using electrical measurements. A detailed comparison between both sample types in terms of current-voltage, external quantum efficiency and photoluminescence measurements show very different optoelectronic behaviour which is indicative of a successful passivation. SCAPS simulations are done to explain the observed results in view of passivation of the rear interface.