Stress relaxation of commercial poly(vinyl chloride) (PVC) is measured at strains below 3% and at different temperatures below the glass transition temperature. First it is shown that below the yield point the material follows a linear viscoelastic behavior. Then the data at a fixed deformation level (0.03) are fitted by considering a lognormal distribution function of relaxation times. Furthermore, from the measured stress-strain curves, the temperature dependence of the elastic tensile modulus is determined. The temperature dependence of the elastic modulus, the relaxation strength, and the parameters of the distribution : mean relaxation time, tau(m), and half-width, beta, are given. Moreover, the distribution function and the temperature dependence of its characteristic parameters are discussed in terms of a cooperative model of the mechanisms involved in the mechanical relaxation of glassy polymers. Finally, the relationship proposed between the tensile modulus and the free volume helps explain the temperature dependence of the relaxation strength.