This paper presents optimisation of rear Si texturing by KOH-based solution for enhanced light-trapping in liquid-phase crystallised Si thin-film solar cells on glass. Texturing with 3 mu m Si removal exhibits the largest absorption enhancement (compared with 1 and 2 mu m Si removal) due to the enhanced light scattering by the rear pyramidal features. In the solar cells with SiOx/SiNx/SiOx buffer layer (with anti-reflection effect), the J(sc) is found to increase from 20.4 (planar reference) to 22.6 mA/cm(2) (10.8% enhancement) with the optimised rear Si texturing. The V-oc and pFF are not degraded. After incorporating white paint back surface reflector and front anti-reflection foil to the rear-textured solar cells, J(sc) up to 25.4 mA/cm(2) (24.5% relative enhancement) is achieved.