Isotropicnematic (IN) transitions in cellulose nanocrystal (CNC) suspension and self-assembled structures in the isotropic and nematic phases were investigated using scattering and microscopy methods. A CNC suspension with a mass fraction of 7.4% spontaneously phase separated into an isotropic phase of 6.9% in the top layer and a nematic phase of 7.9% in the bottom layer. In both the phases, the CNC particles formed stacks with an interparticle distance being of approximate to 37 nm. One-dimensional small-angle neutron scattering (SANS) profiles due to both phases could be fitted using a stacking model considering finite particle sizes. SANS and atomic force microscopy studies indicate that the nematic phase in the bottom layer contains more populations of larger particles. A weak magnetic field of approximate to 0.5 T was able to induce a preferred orientation of CNC stacks in the nematic phase, with the stack normals being aligned with the field (perpendicular to the long axis of CNC particles). The Hermans orientation parameter, , was approximate to 0.5 for the nematic phase; it remained unchanged during the relaxation process of approximate to 10 h. The fraction of oriented CNC populations decreased during the relaxation; dramatic decrease occurred in the first 3 h. The top layer remained isotropic in the weak field. Polarized microscopy studies revealed that the nematic phase was chiral. Adjacent particles in a stack form a twisting angle of approximate to 0.6 degrees, resulting in a helix pitch distance of approximate to 22 mu m.