In the past decades, many efforts have been devoted to characterizing {001} platelet defects in type Ia diamond. It is known that N is concentrated at the defect core. However, an accurate description of the atomic structure of the defect and the role that N plays in it is still unknown. Here, by using aberration-corrected transmission electron microscopy and electron energy-loss spectroscopy we have determined the atomic arrangement within platelet defects in a natural type Ia diamond and matched it to a prevalent theoretical model. The platelet has an anisotropic atomic structure with a zigzag ordering of defect pairs along the defect line. The electron energy-loss near-edge fine structure of both carbon K-and nitrogen K-edges obtained from the platelet core is consistent with a trigonal bonding arrangement at interstitial sites. The experimental observations support an interstitial aggregate mode of formation for platelet defects in natural diamond.