This study demonstrated the application of a new type of interlayer-free cobalt-doped silica membrane in treating ammonia solutions by pervaporation applied towards wastewater treatment. For enhanced hydro-thermal stability, cobalt-doped silica (CoSi) membranes with increasing cobalt concentrations from 1 to 35 mol% were prepared and evaluated, namely CoSi-1, 5, 20 and 35. These membranes exhibited high water fluxes of 66 Lm(-2) h(-1) for CoSi-1 and 15.5 Lm(-2) h(-1) for CoSi-35 at 45 degrees C. The fluxes of the membranes decreased with increasing cobalt concentration; while the rejection to total nitrogen (TN, ammonia nitrogen) increased and hence allowed selective passage of water molecules. Enhanced thermostability was observed for the membranes, particularly CoSi-35 that exhibited TN rejection up to 99% at high temperature of 65 degrees C and highly alkaline environment (pH > 10). Also, the CoSi-35 membrane showed stable performance in treating ammonia present in industry wastewater by achieving stable TN and mineral rejections of 97% and 99%, respectively. Fouling was observed and confirmed by SEM morphological analysis and EDX elemental inspection. The results indicated the deposition of low solubility salts such as CaSO4.