The Ag-Cu-In thermodynamic material system is of interest for brazing alloys and chalcopyrite thin-film photovoltaics. To advance these applications, Ag-Cu-In was assessed and a Calphad model was developed. Binary Ag-Cu and Cu-In parameters were taken from previous assessments, while Ag-In was re-assessed. Structure-based models were employed for beta-bcc(A2)-Ag3In, gamma-Ag9In4, and AgIn2 to obtain good fit to enthalpy, phase boundary, and invariant reaction data for Ag-In. Ternary Ag-Cu-In parameters were optimized to achieve excellent fit to activity, enthalpy, and extensive phase equilibrium data. Relative to the previous Ag-Cu-In assessment, fit was improved while fewer parameters were used.