Premixed and diffusion dust flames of zinc particles dispersed in the gas (particle size d(10)=4.4 mu m; metal mass concentration C-f=0.40kg/m(3)) with propane additives of molar concentration C-g=(2-8)% are studied. Two different burning modes of zinc gas suspension are found. The conditions of formation of these modes depend on the burning temperature of such systems. Two-zone structure of the flamea zinc evaporation and combustion zone and a zinc vapor condensation zoneis observed. Its origin is explained by the unique specificity of a zinc burning process in contrast to other metalszinc vapor does not react with oxygen in the gaseous phase, therefore, ZnO molecules and zinc oxide clusters are absent in the combustion zone. The morphology and dispersive composition of the condensed zinc oxide also depend on the gas suspension's burning mode. In a low-temperature burning mode of zinc dust, the combustion products mostly contain tetrapods, needles and nanorods of zinc oxide. At higher temperatures of the flame, zinc oxide nanorods prevail.