Large-area ZnO/Cu2O heterojunction have been successfully synthesized on Cu foil through a simple two-step solution method at near room temperature. The field emission scanning electron microscopy characterization indicates that the morphology of as-prepared Cu2O film grown on Cu foil is octahedral structure with diameter of similar to 450 nm and ZnO is nanorod arrays structure with diameter of similar to 150 nm. The current-voltage measurement of ZnO/Cu2O heterojunction shows a typical rectifying characteristics. Moreover, the photocatalytic test indicates that ZnO/Cu2O heterojunction exhibits high photocatalytic efficient for degradation of congo red dyes. The possible photocatalytic mechanism of ZnO/Cu2O heterojunction is also presented. (C) 2017 Elsevier B. V. All rights reserved.